Ni61Mössbauer study of the hyperfine magnetic field near the Ni surface
$^{61}\mathrm{Ni}$ M\"ossbauer measurements have been performed at 4.2 K on spherical Ni particles covered with a protective layer of SiO, with average diameter of 500 and 50 \AA{}. The hyperfine magnetic field at $^{61}\mathrm{Ni}$ nuclei for 500-\AA{} particles has been found to be 78.3(4) kOe, compared with the field for Ni foil of 75.0(2) kOe. The small difference is due to the demagnetization and dipolar fields in 500-\AA{} particles. The spectrum of 50-\AA{} particles has a surface component with the corresponding value of the hyperfine magnetic field of 40.3(5.4) kOe. This strongly indicates that, in accordance with recent theoretical studies, there is a decrease of the hyperfine mag…
57Fe,61Ni, and121Sb M�ssbauer study of oxidic spinel ferrites CoxNi5/3?xFeSb1/3O4
Antimony substituted nickel ferrites Co x Ni5/3−xFeSb1/3O4 withx=0,1/3,1,4/3, and 5/3 were prepared by the common ceramic technique, and the single-phase structure was confirmed by x-ray powder diffraction.57Fe Mossbauer spectra were recorded at 4.2 K with and without an applied magnetic fieldHlong=60 kOe in order to determine the cation distribution and the spin structure. Utilizing the cation distributions and the Yafet-Kittel spin structures for B-site Fe3+ ions, derived from Mossbauer experiments the calculated magnetic moments are in excellent agreement with the experimental values at 4.2 K. The existence of Ni2+ ions in crystallographic A-sites was confirmed by61Ni Mossbauer spectrosc…
Ni participation in the magnetism of Fe-Ni-Si-B amorphous alloys.
$^{61}\mathrm{Ni}$ M\"ossbauer measurements at 4.2 K have been performed on (${\mathrm{Fe}}_{\mathrm{x}}$${\mathrm{Ni}}_{1\mathrm{\ensuremath{-}}\mathrm{x}}$${)}_{77}$${\mathrm{Si}}_{1013}$ amorphous alloys with x=0.0, 0.1, and 0.9. Ni atoms in ${\mathrm{Ni}}_{77}$${\mathrm{Si}}_{10}$${\mathrm{B}}_{13}$ bear no magnetic moment, whereas in (${\mathrm{Fe}}_{0.1}$${\mathrm{Ni}}_{0.9}$${)}_{77}$${\mathrm{Si}}_{10}$${\mathrm{B}}_{13}$ and (${\mathrm{Fe}}_{0.9}$${\mathrm{Ni}}_{0.1}$${)}_{77}$${\mathrm{Si}}_{10}$${\mathrm{B}}_{13}$ their moments are, respectively 0.38${\ensuremath{\mu}}_{B}$ and 0.65${\ensuremath{\mu}}_{B}$. Our results, together with the literature data, show that Ni atoms in Fe-…