Influence of thickness and translucency of lithium disilicate ceramic on degree of conversion of resinous materials
Background In this study was assessed the degree of conversion (DC) of amine-free resin cements light cured through lithium disilicate-reinforced ceramics at different thicknesses and translucency. Material and Methods Specimens were divided into 21 groups (n = 5) according to luting agent used: Variolink Esthetic LC (Light shade), RelyX Ultimate (A1 shade), and Filtek Z350 XT Flow (A1 shade); the ceramic translucency: low (LT) and high (HT); and the ceramic thickness: no ceramic (control), 0.5 mm, 1 mm, and 2 mm. A Teflon mold with (5 x 5 x 0.5 mm) was used to standardize the cement and over it the ceramic block from each group was placed. Set was cured using a polywave LED light (1200 mW/…
Minimal intervention in dentistry: Which is the best approach for silorane composite restoration repairs?
Made available in DSpace on 2021-06-25T10:28:11Z (GMT). No. of bitstreams: 0 Previous issue date: 2021-04-01 Background: This study aimed to evaluate surface treatments, adhesives and composites for repairing silorane based restorations. Material and Methods: One hundred and twenty truncated cones (2 mm smaller diameter and 4 mm larger diameter) made of silorane composite were divided in 12 groups according with the surface treatment (diamond bur and oxide aluminum abrasion), the adhesive (Adper Scothbond Multipurpose (3M ESPE), Ecusit (Voco) and Filtek P90 Adhesive (3M ESPE)). Each group was subdivided in two according with the composite used for repair (methacrylate and silorane). The rep…