Experimental Comparison of the MIG and Friction Stir Welding Processes for AA 6005 Aluminium Alloy
In this study, the mechanical properties of welded joints of AA 6005 aluminum alloy obtained with friction stir welding (FSW) and conventional metal inert gas welding (MIG) are studied. FSW welds were carried out on a semi-automatic milling machine. The performance of FSW and MIG welded joints were identified using tensile and bending impact tests, as far as the environmental aspects are also included in the discussion. The joints obtained with FSW and MIG processes were also investigated in their microstructure. The results indicate that, the microstructure of the friction stir weld is different from that of MIG welded joint. The weld nugget consists of small grains in FSW than those found…
An Experimental Investigation of Residual Stresses in Hard Machining of AISI 52100 Steel
In this paper an experimental investigation was conducted to determine the effects of the tool cutting-edge geometry, workpiece hardness, cutting speed, and microstructural changes (white and dark layers) on the residual stresses in dry orthogonal hard machining of AISI 52100 steel. X-ray diffraction technique was used to obtain in-depth residual stresses profiles in both axial and circumferential directions. The results show that tool geometry, workpiece hardness and cutting parameters significantly affect the surface residual stress, maximum compressive residual stress below the machined surface and its location. Moreover, microstructural analysis shows that thermally-induced phase transf…