Effect of film thickness on the transport properties of MgB2 synthesized by spray pyrolysis
Abstract Polycrystalline MgB2 films of different thickness have been prepared by employing spray pyrolysis technique on MgO (1 0 0) substrate. The MgB2 and other phases have been confirmed using X-ray diffraction technique and no trace of impurities phases have been found. The resistivity behavior shows that the superconducting transition temperature lies in the range of 37–39 K with narrow transition width. The transport critical current density vary with films thickness and achieved highest value ∼1.2 × 106 A/cm2 at 20 K for 2.0 μm thick film and its values increase as thickness increases.
Large Zero-Field Cooled Exchange-Bias in BulkMn2PtGa
We report a large exchange-bias (EB) effect after zero-field cooling the new tetragonal Heusler compound Mn2PtGa from the paramagnetic state. The first-principle calculation and the magnetic measurements reveal that Mn2PtGa orders ferrimagnetically with some ferromagnetic (FM) inclusions. We show that ferrimagnetic (FI) ordering is essential to isothermally induce the exchange anisotropy needed for the zero-field cooled (ZFC) EB during the virgin magnetization process. The complex magnetic behavior at low temperatures is characterized by the coexistence of a field induced irreversible magnetic behavior and a spin-glass-like phase. The field induced irreversibility originates from an unusual…
Structure and electrical resistivity of mixed-valent EuNi2P2 at high pressure.
The structural properties and electrical resistivity of homogeneous mixed-valent EuNi2P2 are studied at pressures up to 45 GPa. No structural phase transition is observed in the whole pressure range and the overall pressure behavior of the structural parameters is similar to that of related compounds in the collapsed tetragonal ThCr2Si2-type structure. Electrical resistivity measured up to 31 GPa at temperatures between 4 and 300 K exhibits continuous changes from the behavior typical for a mixed-valent Eu system to that of a normal metallic system at pressures above 20 GPa, indicating a transition of the strongly mixed-valent Eu atoms with a valence ~2.5 towards a pure trivalent state. No …