Excitation and photoluminescence spectra of single- and non-single-phased phosphors based on LaInO3 doped with Dy3+, Ho3+ activators and Sb3+ probabl…
2017
Abstract Single-phased La 0.95 Ln 0.05 InO 3 ( Ln – Dy, Ho), La 0.90 Dy 0.05 Ho 0.05 InO 3 , LaInO 3 ceramic samples as well as the La 0.95 Ln 0.05 In 0.98 Sb 0.02 O 3 ( Ln – Dy, Ho), La 0.90 Dy 0.05 Ho 0.05 In 0.98 Sb 0.02 O 3 , LaIn 0.98 Sb 0.02 O 3 samples with additional impurity LaSbO 3 phase were prepared by solid-state reactions method. Their excitation and photoluminescence (PL) spectra were measured at room temperature. It was established that PL bands intensity of spectra obtained for samples of nominal composition La 0.95 Dy 0.05 In 0.98 Sb 0.02 O 3 , La 0.95 Ho 0.05 In 0.98 Sb 0.02 O 3 , La 0.90 Dy 0.05 Ho 0.05 In 0.98 Sb 0.02 O 3 is much higher than that of single-phase La 0.95…
Excitation and emission spectra of LaInO3-based solid solutions doped with Sm3+, Sb3+
2017
Abstract X-ray analysis showed that all the ceramic samples of La 1- x Sm x InO 3 (0.010≤ x ≤0.025) solid solutions were single-phased but the samples of nominal composition of LaIn 0.98 Sb 0.02 O 3 , La 0.98 Sm 0.02 In 0.98 Sb 0.02 O 3 contained a small amount of impurity phase of LaSbO 3 -based solid solutions. It was established that La 0.98 Sm 0.02 InO 3 solid solution under the excitation of 275 nm and 320 nm exhibits the strongest photoluminescence among La 1- x Sm x InO 3 solid solutions with 0.010≤ x ≤0.025. Photoluminescence bands located in wavelength ranges of 550–580 nm, 585–625 nm and 630–680 nm exhibit 2–3 clear maxima each. According to the locations of these maxima we calcul…