L. A. Bashkirov
Excitation and photoluminescence spectra of single- and non-single-phased phosphors based on LaInO3 doped with Dy3+, Ho3+ activators and Sb3+ probable sensitizer
Abstract Single-phased La 0.95 Ln 0.05 InO 3 ( Ln – Dy, Ho), La 0.90 Dy 0.05 Ho 0.05 InO 3 , LaInO 3 ceramic samples as well as the La 0.95 Ln 0.05 In 0.98 Sb 0.02 O 3 ( Ln – Dy, Ho), La 0.90 Dy 0.05 Ho 0.05 In 0.98 Sb 0.02 O 3 , LaIn 0.98 Sb 0.02 O 3 samples with additional impurity LaSbO 3 phase were prepared by solid-state reactions method. Their excitation and photoluminescence (PL) spectra were measured at room temperature. It was established that PL bands intensity of spectra obtained for samples of nominal composition La 0.95 Dy 0.05 In 0.98 Sb 0.02 O 3 , La 0.95 Ho 0.05 In 0.98 Sb 0.02 O 3 , La 0.90 Dy 0.05 Ho 0.05 In 0.98 Sb 0.02 O 3 is much higher than that of single-phase La 0.95…
Temperature and impurity concentration effects on upconversion luminescence in LaInO3 doped with Er3+
In this paper a novel method for synthesis of LaInO3:Er3+ is reported and upconversion luminescence properties of the synthesized material at different temperatures (9–300 K) are studied. The samples were prepared by co-precipitation and subsequent heat treatment of lanthanum, indium and erbium hydroxides. It is shown that the excitation at 980 nm leads to a strong green upconversion luminescence in the material. At the concentrations above 0.1 mol. % of Er3+ the energy transfer upconversion mechanism of the luminescence becomes evident. Further increase of Er3+ content in the material leads to higher red-to-green upconversion luminescence intensity ratio. The mechanisms responsible for the…