Influence of Electromechanical Fields on Dielectric Properties of PLZT−x/65/35 Ceramics (x = 6 and 7)
High density and transparent PLZT−x/65/35 (x = 6 and 7) ceramics with the average grain size of 5–7 μm was obtained by two−stage hot−pressing technology. The measurements of temperature/frequency dependence of the permittivities of these ceramics under uniaxial pressure (0–100 MPa) applied parallel to the ac electric field have been carried out. It was found that uniaxial pressure significantly influences dielectric properties of these ceramics. With the increase of pressure the maximum intensity in ϵ(T) curve decreases, becomes more diffuse and shifts towards higher temperature, dielectric dispersion decreases and classical ferroelectric seems to change to relaxor one. It was concluded, th…
LEAD-FREE (Na0.5Bi0.5)1-xBaxTiO3 SINGLE CRYSTALS (0 ≤ x ≤ 0.05) AND THEIR DIELECTRIC AND PYROELECTRIC PROPERTIES
ABSTRACT Lead-free single crystals of Na0.5Bi0.5TiO3-BaTiO3 (NBT-BT) system were prepared by Czochralski method and their dielectric and pyroelectric properties have been studied. The results were compared with these for pure NBT. The obtained samples show pure perovskite structure with rhombohedral symmetry at room temperature. Low frequency (100 Hz–100 kHz) investigations reveal the diffuse phase transitions. The obtained results are discussed in terms of local electric and strain fields caused by different ionic radius of (Na, Bi) and Ba ions. The NBT-BT system is expected to be a new promising candidate for lead-free electronic crystals.
Dielectric Properties of Na0.5K0.5(Nb1-xSbx)O3+MnO2 Ceramics (x = 0.04, 0.05 and 0.06)
Lead-free ceramics Na0.5K0.5(Nb1-xSbx)O3+0.5mol%MnO2 (x = 0.04, 0.05 and 0.06) were prepared by conventional sintering and hot pressing process; their microstructure and dielectric properties have been studied. It is found that increase of sintering temperature promotes the obtaining highly dense microstructure and increase in grain size while doping with Sb contributes to more dense and homogeneous microstructure and smaller grain size. Low frequency (100 Hz-200 kHz) investigations revealed the diffuse phase transitions. It can be concluded from experimental results that Sb doping improves dielectric properties. The obtained materials are expected to be promising candidates for lead-free e…
Electrical Transport Properties of Lead−Free (Na0.5Bi0.5)1-xBaxZr0.04Ti0.96O3Ceramics (x = 0.06, 0.085, 0.1)
Lead-free ceramics (Na0.5Bi0.5)1-xBaxZr0.04Ti0.96O3 were prepared by solid phase hot pressing sintering process. Density values of obtained samples are higher than 95% of the theoretical ones. Samples with x = 0.06, 0.085 and 0.1 were investigated in the present work. For these samples both ac and dc electric conductivity were studied. A low frequency (100 Hz-100 kHz) ac conductivity obeys the power law, characteristic for disordered materials. The dc conductivity has a thermally activated character. A barrier hopping model is found to explain the mechanism of charge transport in these materials. The (Na0.5Bi0.5)1-xBaxZr0.04Ti0.96O3 system is expected to be a new and promising candidate for…
Dielectric and Ferroelectric Properties of Lead-Free NKN and NKN-Based Ceramics
Lead-free ceramics of Na0.5K0.5NbO3 (NKN), Na0.5K0.5(Nb0.94Sb0.06)O3 (NKNS6) and Na0.5K0.5(Nb0.94Sb0.06)O3 + 0.5%MnO2 (NKNS6 + 0.5%MnO2) have been prepared by a solid phase hot pressing sintering process. X-ray diffraction results show that the obtained samples possess the perovskite structure. The micrograph of the fractured surface showed a dense structure in a good agreement with that of 91–94% relative density determined by the Archimedes method. An average grain size decreases with Sb and Mn doping (from about 20 μm for NKN to about 5 and 2 μm for NKNS6 and NKNS6 + 0.5%MnO2, respectively). Low frequency (100 Hz–200 kHz) investigations revealed the diffuse phase transitions. It was foun…
Effect of Electromechanical Loading on the Dielectric Properties of PLZT−x/65/35 Ceramics (x = 8 and 8.5)
The influence of uniaxial pressure (0-800 bars) applied parallel to the ac electric field on the dielectric properties of La−modified lead–zirconate−titanate ceramics with the Zr/Ti ratio of 65/35 was investigated. Applying uniaxial pressure leads to the reduction of the peak intensity of the electric permittivity (ϵ), of the frequency dispersion as well as of the dielectric hysteresis. The peak intensity of ϵ becomes diffuse and shifts with increasing the pressure. Our results show that applying uniaxial pressure induces similar effects as increasing the Ti−ion concentration in PZT system. We interpreted our results based on domain switching processes under the action of combined electrome…
PLZTx/65/35 ceramics (x = 2 and 4) under electromechanical and temperature loading
The effect of uniaxial pressure (0–1000 bars) applied parallel to the ac electric field on dielectric properties of La-modified lead–zirconate–titanate, Pb(Ti,Zr)O3 (PZT), ceramics with Zr/Ti ratio of 65/35 was investigated. The experimental results revealed that applying uniaxial pressure leads to a reduction of the peak intensity of the electric permittivity (e), of the frequency dispersion as well as of the dielectric hysteresis. Moreover, with increasing pressure, the peak intensity of e becomes diffuse and shifts to a higher temperature. It was concluded that applying uniaxial pressure induces similar effects as increasing the Ti–ion concentration in PZT system. The obtained results we…