Study of alite containing aluminium hydration
International audience
Hydration of alite containing alumimium
International audience; The most important phase in cement is tricalcium silicate which leads during its hydration to the nucleation and growth of calcium silicate hydrate (referred to C-S-H (CaO)x-SiO2-(H2O)y). The development of this hydrate around the cement grains is responsible for the setting and hardening of cement pastes The general term for designating the tricalcium silicate in cements is alite. This name relates to all polymorphs containing various foreign ions inserted in their structure. These ions may influence the intrinsic reactivity and once released during the dissolution, they may interact also with C-S-H. The melt phase during clinkering is rich in aluminium and moreover…
Hydration of alite containing aluminium
Abstract The most important phase in Portland cement is tricalcium silicate, which leads during its hydration to the nucleation and growth of calcium silicate hydrate [referred to as C–S–H, (CaO)x–SiO2–(H2O)y]. The development of this hydrate around the cement grains is responsible for the setting and hardening of cement pastes. The general term for designating the tricalcium silicate in cements is alite. This name relates to all polymorphs containing various foreign ions inserted in their structure. These ions may influence the intrinsic reactivity, and once released during the dissolution, they may interact also with C–S–H. One of the most likely species to be inserted in the alite struct…
The influence of an ion-exchange resin on the kinetics of hydration of tricalcium silicate
The addition of a finely-ground ion-exchange resin makes it possible to modify the hydration kinetics of C3S pastes. Analyses of the liquid phase in pastes and more dilute suspensions show that the resin exchanges calcium ions for sodium ions very rapidly during the early stage of hydration and therefore the concentration of silica in solution increases. The resin impacts the hydration of C3S by other mechanisms which depends on the resin quantity added. For a high resin quantity, the induction period is very short, but the longer-term hydration is enhanced compared to a reference sample without resin. We hypothesize that the surface of the resin can provide sites for the nucleation and gro…