Topochemical Reactions of Monomers with Conjugated Triple-Bonds VII Mechanism of Transition from Monomer to Polymer Phase During Solid-State Polymerisation
The lattice-controlled solid-state polymerisation of three different modifications of 2,4-hexadiin-1,6-diol-bis(phenylurethane) was investigated by X-ray and optical methods. The polymerisation is a homogeneous reaction. The polymer grows in the form of single chains within the crystal of the monomer. The chains extend along a definite crystallographic direction. Monomer and polymer are isomorphous and monomer-polymer single crystals of various compositions are obtained up to a quantitative conversion in the case of modification I or III. Phase separation into a mesomorphic polymer and oriented monomer phase was observed on annealing partially polymerised single-crystals of modification II …
Das Wachstum von Polymerketten im Kristallgitter des Monomeren
Einige niedermolekulare Verbindungen mit konjugierten Dreifachbindungen als Strukturelement konnen im festen, kristallinen Zustand polymerisiert werden. Die Polymerisation tritt bei Bestrahlung der Monomerkristalle mit Rontgenoder UV-Licht oder beim Tempern unterhalb des Schmelzpunktes der jeweiligen Monomermodifikation ein (1–3). Es gelingt mit dieser Methode, Einkristalle des Monomeren in Einkristalle des entsprechenden Polymeren umzuwandeln. Dabei ist die Frage von Interesse, wie die Ketten des topochemisch erzeugten Polymeren im Gitter des Monomeren wachsen. Zwei verschiedene Mechanismen sind denkbar: 1. Im Verlauf der topochemischen Polymerisation konnen die Ketten im Monomergitter ein…