Post-sintering heat treatment effect on the coercivity of sintered (Nd,Dy)15(Fe,Co,Mo,Al)77B8 permanent magnets
Abstract The effect of heat treatment on the intrinsic coercivity, iHc and microstructure were investigated for sintered (Nd,Dy)15(Fe,Co,Mo,Al)77 B8 permanent magnet. The microstructure has been investigated by scanning electron microscopy (SEM), energy dispersive X-ray analysis (EDX), X-ray spectroscopy and Mossbauer spectroscopy. The observed behaviour of iHc may be caused by a superposition of the following effects: (i) the distribution of the nonmagnetic phases and the ratio of the amount of hard magnetic Nd2Fe14B-phase to the amount of the residual phases; (ii) homogeneous distribution of elements in the main phases; (iii) removing the stresses in the phases; and (iv) diffusion of Al, …
The effect of less additives on magnetic properties and microstructure of sintered Nd–(Fe,Ti,Al)–B magnets
Abstract The effect of the addition of 0.5 at.% Cu, Ga, Hf, V, Mo, Nb, Co, Ni, Cr, Dy or Tb on the magnetic properties and the microstructure of sintered Nd 16 Fe 75.22 Ti 1.26 Al 0.32 B 7.2 magnets has been studied. It is shown that these additives cause a small decrease in remanence and in intrinsic coercivity, with the exception of Cu, Dy and Tb additives, which lead to an increase in the intrinsic coercivity. The correlation between the hyperfine magnetic field and the magnetic properties of the investigated magnets is discussed.