Crystal structures of superconducting sodium intercalates of hafnium nitride chloride
Sodium intercalation compounds of HfNCl have been prepared at room temperature in naphtyl sodium solutions in tetrahydrofuran and their crystal structure has been investigated by Rietveld refinement using X-ray powder diffraction data and high-resolution electron microscopy. The structure of two intercalates with space group Rm and lattice parameters a = 3.58131(6) A u , c = 57.752(6) A u , and a = 3.58791(8) A u , c = 29.6785(17) A u is reported, corresponding to the stages 2 and 1, respectively, of NaxHfNCl. For the stage 2 phase an ordered model is presented, showing two crystallographically independent (HfNCl) units with an alternation of the Hf-Hf interlayer distance along the c-axis, …
Critical temperature modification of low dimensional superconductors by spin doping
Ion implantation of Fe and Mn into Al thin films was used for effective modification of Al superconductive properties. Critical temperature of the transition to superconducting state was found to decrease gradually with implanted Fe concentration. it was found that suppression by Mn implantation much stronger compared to Fe. At low concentrations of implanted ions, suppression of the critical temperature can be described with reasonable accuracy by existing models, while at concentrations above 0.1 at.% a pronounced discrepancy between the models and experiments is observed.
Anion ordering and defect structure in Ruddlesden-Popper strontium niobium oxynitrides
The crystal structure of the n = 1 member of the Ruddlesden-Popper family (SrO)(SrNbO(2)N)(n) was refined by the Rietveld method using neutron powder diffraction data. This complex crystallizes in the I4/mmm space group with cell parameters a = 4.0506(2) and c = 12.5936(9) angstroms. The refined composition was Sr(2)NbO(3.28)N(0.72), which corresponds to a formal oxidation state for Nb of +4.72, meaning 72% Nb(V) and 28% Nb(IV). The nitrogen atoms order in the equatorial sites of the niobium octahedra according to Pauling's second crystal rule as the more charged anion occupies the site showing the larger bond strength sums. Pauling's second crystal rule is shown to be able to predict the d…