Oxygen defects: The key parameter controlling the activity and selectivity of mesoporous copper-doped ceria for the total oxidation of naphthalene
Mesoporous CeO2 modified by the addition of copper has shown high efficiency for the total oxidation of naphthalene. High activity and 100% selectivity to carbon dioxide throughout the whole range of temperatures studied were achieved for copper loadings of 3.6% and lower. The catalytic behaviour has been related to the concentration of surface oxygen defects. A clear correlation between the concentration of surface oxygen defects (determined by XPS and DRIFTS) and the catalytic performance has been identified. Catalytic activity increased as copper was incorporated into the ceria up to 3.6%. In this range of copper content the copper was incorporated into the cubic fluorite lattice of CeO2…
Total oxidation of naphthalene using bulk manganese oxide catalysts
Several Mn2O3 catalysts have been synthesized using different preparation methods and tested for the total oxidation of naphthalene, a model polycyclic aromatic compound. The catalysts have been characterized by several physico-chemical techniques such as XRD, TPR, XPS, EDX and TEM. The surface area of the catalyst seems to be of paramount importance, since the mass normalized activity of catalysts increases as the surface area of the Mn2O3 catalysts increases. Consequently, a high surface area ordered mesoporous Mn2O3 catalyst, obtained through a nanocasting route using mesoporous KIT-6 silica as a hard template, was the most efficient catalyst for the deep oxidation of naphthalene. In add…
High activity mesoporous copper doped cerium oxide catalysts for the total oxidation of polyaromatic hydrocarbon pollutants
The doping of mesoporous ceria with copper significantly enhances activity for naphthalene total oxidation, the enhanced performance is controlled by the increased concentration of surface oxygen defects.
Influence of the preparation method on the activity of ceria zirconia mixed oxides for naphthalene total oxidation
Cerium/zirconium mixed oxides, with different Ce/Zr ratios, have been synthesised by a co-precipitation method using two different precipitating agents (sodium carbonate and urea) and tested for the total oxidation of naphthalene. Catalysts were characterized by N2 adsorption, XRD, Raman, TPR, XPS and DRIFTS. Ceria prepared by carbonate precipitation had low activity and this is likely to be related to the high concentration of residual surface carbonate that covers catalytic sites and inhibits reaction. For carbonate precipitation, increasing the Zr content to 1% resulted in a significant increase of activity, which is related to the decrease of surface carbonate. Increasing the Zr content…