Influence of a density mismatch on TMPTMA shells nonconcentricity
Some laser target designs require low-density organic foam shells to study fusion on the French high-power laser laser mega joule. Low-density trimethylolpropane trimethacrylate foam shells composed of C, H, and O, 2 mm diameter, 100-μm wall thickness, and 250 mg cm−3 density are synthesized by a microencapsulation technique using a droplet generator. These shells have to reach a sphericity higher than 99.9% and a nonconcentricity (NC) lower than 1%. The wall thickness variation is one of the most difficult specifications to meet. An important factor in reducing this defect is the density matching between the three phases of the emulsion at polymerization temperature. The influence of a den…
Synthesis of low density foam shells for inertial confinement fusion experiments
This work deals with the fabrication process of low density foam shells and the sharp control of their shape (diameter, thickness, density, sphericity, non-concentricity). During this PhD we focused on the non-concentricity criterion which has to be lower than 1%. The shells are synthesized using a microencapsulation process leading to a double emulsion and followed by a thermal polymerization at 60°C. According to the literature, three major parameters, the density of the three phases, the deformations of the shells along the process and the kinetics of the polymerization have a direct influence on the shells non-concentricity. The results obtained showed that when the density gap between …