Industrial applications of the aggregation of block copolymers in supercritical CO 2 : a SANS study
Industrial applications of supercritical carbon dioxide (scCO2) rely upon the rather selective and easily adjustable solvent ability of CO2. CO2 near the critical point is a poor solvent for high molecular weight (HMW) hydrocarbon polymers, while it is a very good solvent for amorphous fluorinated polymers. By increasing the pressure, CO2 becomes a good solvent even for HMW hydrogenated chains. Specially engineered amphiphilic di-block copolymers, with CO2-philic and CO2-phobic portions, are expected to undergo trough a monomer–aggregate transition when the solvent density of the scCO2 changes. Here small-angle neutron scattering (SANS) results are reported for a block copolymer dissolved i…
Structure of diblock copolymers in supercritical carbon dioxide and critical micellization pressure
This paper reports a small angle neutron scattering investigation of micelle formation by fluorocarbon-hydrocarbon block copolymers in supercritical ${\mathrm{CO}}_{2}{(\mathrm{s}\mathrm{c}\ensuremath{-}\mathrm{C}\mathrm{O}}_{2})$ at 65 \ifmmode^\circ\else\textdegree\fi{}C. A sharp unimer-micelle transition is obtained due to the tuning of the solvating ability of ${\mathrm{s}\mathrm{c}\ensuremath{-}\mathrm{C}\mathrm{O}}_{2}$ by profiling pressure, so that the block copolymer, in a semidilute solution, finds ${\mathrm{s}\mathrm{c}\ensuremath{-}\mathrm{C}\mathrm{O}}_{2}$ a good solvent at high pressure and a poor solvent at low pressure. At high pressure the copolymer is in a monomeric state…
Mesoscopic and Microscopic Investigation on Poly(vinyl alcohol) Hydrogels in the Presence of Sodium Decylsulfate
The structure of poly(vinyl alcohol) (PVA) hydrogels formed as a result of freeze/thaw treatments of aqueous solutions of the polymer (11 wt % PVA) in the freshly prepared state is analyzed through the combined use of small (SANS) and ultrasmall (USANS) angle neutron scattering techniques. The structure of these hydrogels may be described in terms of polymer rich regions, with dimensions of the order of 1-2 microm, dispersed in a water rich phase, forming two bicontinuous phases. The PVA chains in the polymer rich phase form a network where the cross-linking points are mainly crystalline aggregates of PVA having average dimensions of approximately 45 A. The structural organization of freeze…