Phonon Scattering through a Local Anisotropic Structural Disorder in the Thermoelectric Solid Solution Cu_2Zn_(1−x)Fe_xGeSe_4
Inspired by the promising thermoelectric properties of chalcopyrite-like quaternary chalcogenides, here we describe the synthesis and characterization of the solid solution Cu(2)Zn(1-x)Fe(x)GeSe(4). Upon substitution of Zn with the isoelectronic Fe, no charge carriers are introduced in these intrinsic semiconductors. However, a change in lattice parameters, expressed in an elongation of the c/a lattice parameter ratio with minimal change in unit cell volume, reveals the existence of a three-stage cation restructuring process of Cu, Zn, and Fe. The resulting local anisotropic structural disorder leads to phonon scattering not normally observed, resulting in an effective approach to reduce th…
Thermoelectric properties of Sr_3GaSb_3 – a chain-forming Zintl compound
Inspired by the promising thermoelectric properties in the Zintl compounds Ca_3AlSb_3 and Ca_5Al_2Sb_6, we investigate here the closely related compound Sr_3GaSb_3. Although the crystal structure of Sr_3GaSb_3 contains infinite chains of corner-linked tetrahedra, in common with Ca_3AlSb_3 and Ca_5Al_2Sb_6, it has twice as many atoms per unit cell (N = 56). This contributes to the exceptionally low lattice thermal conductivity (κ_L = 0.45 W m^(−1) K^(−1) at 1000 K) observed in Sr_3GaSb_3 samples synthesized for this study by ball milling followed by hot pressing. High temperature transport measurements reveal that Sr_3GaSb_3 is a nondegenerate semiconductor (consistent with Zintl charge-coun…