Synthesis and characterization of praseodymium-containing ZrSiO4 solid solutions from gels
Abstract The preparation and characterization of a series of praseodymium–zircon solid solution (Prx–ZrSiO4) materials with increasing nominal amounts of Pr is reported. Pr-doped zircon gels were prepared by gelling mixtures of zirconium n-propoxide, praseodymium acetylacetonate and tetraethylorthosilicate, and annealed over the range of temperature up to the formation of Pr–zircon solid solutions. The reaction sequence was followed by X-ray powder diffraction (XRD), ultraviolet–visible diffuse reflectance (DR) and infrared spectroscopy (IR). The first crystalline phase detected on annealing gels was a tetragonal praseodymium-containing ZrO2 phase (t-Pr–ZrO2). On further annealing, the subs…
Effect of zinc concentration on the microstructure and relaxation frequency of Mn–Zn ferrites synthesized by solid state reaction
Abstract Mn3Zn polycrystalline ferrites with Mn1−xZnxFe2O4 stoichiometry (x=0.59, 0.61, 0.65) were prepared by solid state reaction. These ferrites were heated at different temperatures. The cubic structure with space group Fd3m (Oh7) No. 227 was confirmed by the refinement of x-ray diffraction (XRD) powders through Rietveld´s method using fullprof. Scanning electron microscopy (SEM) results revealed for all compounds a non-homogeneous grain size and shape distribution, with a mean grain size of 9 μm. The Curie temperature Tc was found to decrease as the Zn concentration increases. The magnetic domain relaxation was investigated by inductance spectroscopy (IS). The relaxation frequency fr s…
Layered-structural monoclinic–orthorhombic perovskite La2Ti2O7 to orthorhombic LaTiO3 phase transition and their microstructure characterization
The layered-structural ceramics, such as lanthanum titanate (La{sub 2}Ti{sub 2}O{sub 7}), have been known for their good temperature and low dielectric loss at microwave frequencies that make them good candidate materials for high frequency applications. However, few studies have been conducted on the synthesis optimization by sol gel reaction, in particular by acrylamide polymerization route. The interest in La{sub 2}Ti{sub 2}O{sub 7} ceramic has been greatly increased recently due to the effect of oriented grains. This anisotropy of the microstructure leads to anisotropy in dielectric, electrical and mechanical properties. In this study, grain oriented lanthanum titanate was produced by t…
Synthesis and Characterization of Iron-Doped ZrSiO4 Solid Solutions from Gels
The mechanism of formation and the structural features of tetragonal Fe–ZrO2-amorphous silica composites and particulated Fe-doped ZrSiO4 solid solutions were studied. A series of specimens with compositions Fex–ZrSiO4, 0 ≤ x ≤ 0.10 were prepared by sol–gel techniques and thermally annealed over the range of temperature between 400°C and 1600°C. Results confirmed the formation of tetragonal Fe–ZrO2 solid solution as first crystalline phase on the whole process leading to Fe-doped ZrSiO4 solid solution. The annealing temperature for the preparation of Fe-containing ZrSiO4 solid solutions was dependent on the nominal amount of iron. The Fex–ZrSiO4 solid solutions, with 0.02 < x < 0.08, were a…
Microstructure of Fe–ZrSiO4 solid solutions prepared from gels
Abstract Microstructural changes associated with chemical and structural evolution from gels to Fe x –ZrSiO 4 solid solutions are reported. Mineralizer-free Fe x –ZrSiO 4 gels in the compositional range 0 ≤ x ≤ 0.15 were prepared by sol–gel liquid-phase route from mixtures of alkoxides of silicon and zirconium, and iron (III) acetylacetonate, and annealed at different temperatures and/or times. The first step on the whole process to the final Fe x –ZrSiO 4 solid solutions was the formation of aggregated of tetragonal Fe-doped ZrO 2 nanocrystals with diameters smaller than 50 nm. At this stage the tetragonal Fe–ZrO 2 were embedded in amorphous silica resulting nanocomposite materials. The …