Crystal Reorientation and Amorphization Induced by Stressing Efficient and Stable P–I–N Vacuum‐Processed MAPbI 3 Perovskite Solar Cells

Herein, the long-term stability of vacuum-deposited methylammonium lead iodide (MAPbI(3)) perovskite solar cells (PSCs) with power conversion efficiencies (PCEs) of around 19% is evaluated. A low-temperature atomic layer deposition (ALD) Al2O3 coating is developed and used to protect the MAPbI(3) layers and the solar cells from environmental agents. The ALD encapsulation enables the MAPbI(3) to be exposed to temperatures as high as 150 degrees C for several hours without change in color. It also improves the thermal stability of the solar cells, which maintain 80% of the initial PCEs after aging for approximate to 40 and 37days at 65 and 85 degrees C, respectively. However, room-temperature…