Quaternary ammonium polyiodides as ionic liquid/soft solid electrolytes in dye-sensitized solar cells
Abstract Four new quaternary ammonium iodides, (Me 2 Pe 2 N)I, (Me 2 Hex 2 N)I, (Et 2 Pe 2 N)I and (Et 2 Hex 2 N)I, were synthesized and studied as electrolytes in dye-sensitized solar cells. All compounds were solids at room temperature. Influence of varying amounts of elemental iodine and the effect of tert -butylpyridine (TBP) on the performance of the cell was also studied. Addition of iodine lowered the melting points of the resulting polyiodides. From the ammonium iodides only (Me 2 Hex 2 N)I:I 2 (10:1) was liquid at the room temperature and the others were soft solids. Under illumination from a halogen lamp source at 10 mW cm −2 intensity, the highest power conversion efficiency of 2…
Dynamic preparation of TiO2 films for fabrication of dye-sensitized solar cells
Preparation of nanocrystalline porous titanium dioxide (TiO2) films with roll-to-roll compatible methods was studied. Gravure printing was used for spreading TiO2 paste and paper calendering for pressing TiO2 nanoparticle films. Influence of different preparation methods on performance of fabricated dye-sensitized solar cells (DSSCs) was investigated. The attained light into electricity conversion efficiency was compared with DSSCs fabricated on conductive plastic substrates by doctor-blading spreading with subsequent static pressing. The latter method achieved a light conversion efficiency as high as 5.1%. The efficiency of the cells with a gravure printed TiO2 film was found to be rather …