Casein phosphopeptide-amorphous calcium phosphate effects on brackets shear bond strength and enamel damage
2017
Background The aim of study was to evaluate the application of casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) and fluoride regarding their effect on the shear bond strength (SBS), bond failure pattern of brackets using the adhesive remnant index (ARI) and assessing the quality of enamel surface using the enamel damage index (EDI). Material and methods Sixty extracted premolar teeth were randomly divided into four groups regarding pretreatment application of CPP-ACP and fluoride. Brackets were bonded using the conventional method. Specimens were thermocycled for 1000 cycles and were subsequently tested for the SBS in a universal testing machine. After debonding, the teeth were e…
Dentin bonding agent with improved bond strength to dentin through incorporation of sepiolite nanoparticles.
2017
Background The study aims to investigate the effect of incorporation of sepiolite nanoparticles on the microtensile bond strength of an experimental dentin bonding to the human dentin. Material and methods The sepiolite nanoparticles were incorporated into an experimental methacrylate-based dentin bonding system in concentrations of 0.0, 0.2, 1.0, 2.0, and 5.0 weight percents. The specimens were then ultrasonicated to finely disperse the nanoparticles in the adhesive matrix. The coronal enamel of 30 intact human premolars was cut to expose dentin. Having etched, rinsed, and blot dried the experimental bonding agents were applied to dentin surface. Adper Single Bond was used as control group…
Effect of rinsing time and surface contamination on the bond strength of silorane-based and dimethacrylate-based composites to enamel
2018
Background The aim of this study was to assess whether saliva contamination and rinsing time for 15, 30, and 60 seconds, affects the shear bond strength of silorane and methacrylate-based composites to enamel. Material and Methods Two light cure resin, P60 (3M ESPE) and Filtek LS Silorane were tested. 120 sound premolars were randomly divided into four groups of 30 teeth based on composite type with or without saliva contamination after etching and rinsing. Each group was further divided into three subgroups according to their rinsing time. Then a cylinder of the composite was bonded to the enamel and Shear bond strength was assessed. To determine the failure mode, the bonded surfaces were …
Shear bond strength of orthodontic metal brackets to aged composite using three primers
2017
Background This study aimed to assess the effect of surface preparation with sandblasting and diamond bur along with the use of three primers on shear bond strength (SBS) of metal brackets to aged composite. Material and methods In this in vitro, experimental study, 60 Filtek Z250 composite discs were fabricated (10×2mm), immersed in distilled water for 24 hours and subjected to 5000 thermal cycles. They were randomly divided into two groups (n=30) of sandblasting with aluminum oxide particles for 10 seconds and surface roughening with bur. Each group was randomly divided into three subgroups (n=10) for use of Transbond XT, Assure Plus and Composite Primer. Metal brackets were bonded and th…