Preparation, Characterization and Photocatalytic Activity of TiO2 Impregnated with the Heteropolyacid H3PW12O40: Photo-assisted Degradation of 2-propanol in Gas-Solid Regime
Abstract Both commercial and home prepared TiO2 samples impregnated with tungstophosphoric acid (H3PW12O40) were prepared and used for the photo-assisted degradation of 2-propanol in gas–solid regime. The characterization results evidenced a good coverage of the polyoxometalate (POM) onto the surface of both types of TiO2 samples along with a marginal effect of the presence of ethanol or HCl during the POM impregnation step on the specific surface area, porosity, morphology, crystallinity and acidity of the samples. Propene was the main intermediate product found in 2-propanol photocatalytic degradation by using the samples containing POM as the photocatalyst, whereas propanone was mainly o…
Photoactivity of Nanostructured TiO2 Catalysts in Aqueous System and their Surface Acid-Base, Bulk and Textural Properties
This work reports on the characterisation and determintion of the photocatalytic activity of some TiO2 catalysts prepared using TiCl4 as precursor. The samples, consisting of suspensions, dispersions or powders of nanonstructured anatase or rutile phases, were obtained in very mild conditions, i.e., by boiling the solution obtained after hydrolysis of TiCl4 at atmospheric pressure: it is worth noting that no calcination was necessary to obtain photoactive phases. The samples were characterised by X-ray diffraction (XRD), determination of the BET specific surface area (SSA), scanning electron microscopy (SEM) observations and diffuse reflectance spectroscopy (DRS). FT-IR spectroscopy was use…
Zn,Al hydrotalcites calcined at different temperatures: Preparation, characterization and photocatalytic activity in gas–solid regime
Abstract Layered double hydroxides (LDH) containing zinc and aluminium within the brucite-like layers and carbonate as the interlayer anion have been used as precursors for the preparation of mixed metal oxides by calcination. Zinc oxide and the ZnAl 2 O 4 spinel were formed with different degree of crystallinity depending of two parameters, i.e., the Zn 2+ /Al 3+ molar ratio and the calcination temperature (500–800 °C) of the LDH precursor. A pure spinel phase was obtained to remove ZnO upon a basic post-treatment in NaOH solution of the samples calcined at 800 °C. All the samples were tested for the photodegradation of 2-propanol in gas–solid regime. All the samples resulted active as het…
Inorganic gels as precursors of TiO2 photocatalysts prepared by low temperature microwave or thermal treatment
Abstract A simple procedure for preparing active TiO2 photocatalysts is presented. The starting materials were unusual TiO2 gels formed from TiCl4. The use of microwaves for a very short time enhanced the TiO2 crystallinity preventing an increase of particle size and minimizing the decrease of specific surface area. This result makes this preparation very attractive. The formation of the gels was monitored through measurements of viscosity. All the samples were characterized by means of X-ray diffraction, diffuse reflectance spectroscopy and BET specific surface area measurements. The photoactivity of the samples was evaluated using the photodegradation of 4-nitrophenol in liquid–solid regi…
Tungstophosphoric acid supported on polycrystalline TiO2 for the photodegradation of 4-nitrophenol in aqueous solution and propan-2-ol in vapour phase
Abstract The present work reports the preparation of samples based on Millennium PC-500 TiO 2 loaded with different amounts of tungstophosphoric acid (up to 30% in weight) and their characterisation by means of different physicochemical techniques: powder X-ray diffraction, N 2 adsorption–desorption at −196 °C, transmission electron microscopy, UV–vis and FT-IR spectroscopies and thermogravimetric analyses. The acidity of samples was evaluated by FT-IR using pyridine as probe molecule, and the catalysts activity was tested for the photodegradation of 4-nitrophenol in aqueous solution and for the photo-oxidation of propan-2-ol in vapour phase. The results show a noticeable improvement (8 and…