Improved hydrophobicity of inorganic–organic hybrid mesoporous silica with cage-like pores
International audience; Hydrophobic ordered mesoporous silica particles with cage-like pores (SBA-1 type) were prepared through co-condensation of phenyltriethoxysilane (PhTES) and tetraethylorthosilicate (TEOS) at different TEOS/PhTES molar ratios. It is shown that the hydrophobic character of the particles is enhanced by increasing the phenyl loading (decreasing the TEOS/PhTES molar ratio) and that it could be further enhanced by subsequent trimethylsilyl (TMS) grafting on remaining silanol groups (TMS-PhSBA-1 sample). This increase of hydrophobicity has been evidenced on the internal surface (mesoporosity) of the particles using water adsorption and, on the external surface of the partic…
Unusual hysteresis loop in the adsorption-desorption of water in NaY zeolite at very low pressure.
International audience
Temperature-Induced Structural Transitions in the Gallium-Based MIL-53 Metal–Organic Framework
We report a structural and thermodynamic investigation of the phase behavior of Ga(OH,F)-MIL-53, a gallium-based metal–organic framework (MOF) having the MIL-53 topology containing 0.7 wt % fluorine bonded to the metal. Despite some small structural differences, especially for the hydrated form, the overall physical chemistry behavior of Ga(OH,F)-MIL-53 is very similar to standard fluorine free Ga-MIL-53 material. A combination of in situ X-ray diffraction, in situ Fourier transform infrared spectroscopy, differential scanning calorimetry, and heat capacity measurements allowed us to establish that Ga(OH,F)-MIL-53 under vacuum (i.e., the empty material) exhibits two stable phases: a nonporo…
IM-17: a new zeolitic material, synthesis and structure elucidation from electron diffraction ADT data and Rietveld analysis
International audience; The synthesis and the structure of IM-17, a new germanosilicate with a novel zeolitic topology, prepared hydrothermally with decamethonium as the organic structure directing agent, are reported. The structure of calcined and partially rehydrated IM-17 of chemical formula per unit cell |(H2O)14.4|[Si136.50Ge39.50O352] was solved ab initio using electron diffraction ADT data in the acentric Amm2 (setting Cm2m) space group and refined by the Rietveld method. This new zeolite framework type contains a 3D pore system made of intersecting 12, 10 and 8-ring channels.