Nodular cast iron fatigue lifetime in cyclic plane bending
2012
The fatigue behavior of a component is strongly dependent on the material and its surface condition. Therefore, the manner in which the surface is prepared during component manufacturing (surface roughness, residual stresses etc.) has a decisive role in dictating the initiation time for fatigue cracks. The fatigue behavior of the same material, a nodular cast iron, with three different surface conditions (fine ground, sand blast and as-cast) has been investigated under cyclic plane bending. The results show differences in fatigue strength, which are associated with the surface conditions. The characteristics of the surface layers of the different test specimens were examined by metallograph…
FATIGUE CRACK PROPAGATION THROUGH AUSTEMPERED DUCTILE IRON MICROSTRUCTURE
2010
Austempered ductile iron (ADI) has a wide range of application, particularly for castings used in automotive and earth moving machinery industries. These components are usually subjected to variable dynamic loading that may promote initiation and propagation of fatigue cracks up to final fracture. Thus, it is important to determine the fatigue crack propagation behavior of ADI. Since fatigue crack growth rate (da/dN) vs. stress intensity factor K data describe fatigue crack propagation resistance and fatigue durability of structural materials, da/dN vs. Ka curves of ADI 1050 are reported here. The threshold amplitude of stress intensity factor Kath is also determined. Finally, the influence…