Bond strength of a new Kevlar fiber-reinforced composite post with semi-interpenetrating polymer network (IPN) matrix

Background This study aimed to evaluate the bond strength and the penetration depth of two adhesive systems to a new experimental semi-IPN fiber post versus a commercial post. Material and Methods Experimental Kevlar fiber (KF) and control everStick®POST (ES) posts (n=20/ group) with a diameter of 1.5 mm were used, 10 posts coated with StickResin (SR) and the other 10 posts coated with Scotch bond multipurpose (SBMP) adhesives. Composite resin buildup was performed over each post, using a cylindrical plastic mold (10 mm × 6 mm). Four discs of 2 mm thickness were prepared from each post/composite buildup and underwent pushout bond strength test at a crosshead speed of 0.5 mm/min accompanied …