Effect of zinc concentration on the microstructure and relaxation frequency of Mn–Zn ferrites synthesized by solid state reaction
Abstract Mn3Zn polycrystalline ferrites with Mn1−xZnxFe2O4 stoichiometry (x=0.59, 0.61, 0.65) were prepared by solid state reaction. These ferrites were heated at different temperatures. The cubic structure with space group Fd3m (Oh7) No. 227 was confirmed by the refinement of x-ray diffraction (XRD) powders through Rietveld´s method using fullprof. Scanning electron microscopy (SEM) results revealed for all compounds a non-homogeneous grain size and shape distribution, with a mean grain size of 9 μm. The Curie temperature Tc was found to decrease as the Zn concentration increases. The magnetic domain relaxation was investigated by inductance spectroscopy (IS). The relaxation frequency fr s…