CATALYTIC OXIDE COATINGS ON CERAMIC SUPPORTS.
Thin porous oxide coatings composed of Al2O3, SiO2, TiO2 and ZrO2, respectively, on ceramic carriers have been produced by either a wash-coat procedure or by liquid coating followed by solidification. By dehydration and calcination of the supported ceramics the pore texture was stabilised. The thickness of the layer, its homogeneity, specific surface area, porosity and pore volume distribution have been shown to be controlled by the properties of the oxides deposited, and by the conditions of the coating procedures. On the basis of the results obtained, it is evident that porous oxide layers can be prepared with tailor-made and desired properties. The procedures described also permit the in…
Effect of Impregnation and Activation Conditions of Al2O3/CuO Supported Monolith Catalysts in the Reduction of NO
Reduction of NO in the presence of CO and Ar was examined on two series of monolithic sheets carrying an active CuO/Al 2 O 3 layer. In the impregnation procedure the ratio of Al 2 O 3 to CuO was varied in a wide range. The texture of the layer and the dispersion of CuO therein was controlled by mercury porosimetry, scanning electron microscopy and secondary ion mass spectrometry (SIMS). It could be established that the surface concentration of CuO determined by SIMS measurements is the most decisive quantity of the catalyst correlating linearly with the conversion of NO.