The effect of thickness on the composition of passive films on a Ti–50Zr at% alloy
Abstract Anodic films were grown potentiodynamically in different electrolytes (pH = 1–14) on a Ti–50Zr at% cast alloy, obtained by fusion in a voltaic arc under argon atmosphere. The thickness of the films was varied by changing formation potential from the open circuit potential up to about 9 V; growth was followed by 30 min stabilization at the forming potential. Films having different thicknesses were characterized by photocurrent spectroscopy (PCS) and electrochemical impedance spectroscopy (EIS). Moreover, film composition was analyzed by X-ray photoelectron spectroscopy (XPS). Regardless of the anodizing conditions, passive films on the Ti–50Zr at% alloy consist of a single layer mix…
Photo-electrochemical and impedance investigation of passive layers grown anodically on titanium alloys
Abstract The anodic behaviour of two titanium cast alloys, obtained by fusion in a voltaic arc under argon atmosphere, was analyzed in aerated aqueous solutions having different pH values. In all solutions the alloys, having nominal compositions Ti–50Zr at.% and Ti–13Zr–13Nb wt.%, displayed a valve-metal behaviour, owing to the formation of barrier-type oxide films. Passive films, grown potentiodynamically up to about 9 V, were investigated by photocurrent spectroscopy (PCS) and electrochemical impedance spectroscopy (EIS). These passive layers show photoactivity under anodic polarizations, with optical gaps close to 3.55 and 3.25 eV for the binary and the ternary alloy, respectively, indep…