Observation of substitutional Fe in CEMS measurements on synthetic CVD diamond
Conversion electron Mossbauer spectroscopy measurements have been made on a diamond sample synthesized by chemical vapour deposition. The sample was implanted with 70 keV 57Fe to a dose of 5 × 1014 cm−2 and Mossbauer measurements were made on the as-implanted sample and after annealing at temperatures of 600 K, 950 K and 1470 K. The spectra at the lower temperatures were characterized by broad doublets, but the annealing at 1470 K resulted in dramatic decrease in the intensity of the doublet components, and the appearance of a strong single line with an isomer shift of δ = −0.90(5) mm/s and areal intensity of 30%, and a weaker line (5%) with δ = +0.07(4). Arguments are presented to attribut…
CEMS Study of 57Fe Implanted in Diamond
Conversion electron Mossbauer (CEMS) measurements have been made on a diamond sample implanted with 70 keV 57Fe to a dose of 5 × 1014 cm−2. CEMS spectra were collected in the as-implanted state and after annealing the diamond up to 1470 K. The lower temperature spectra were consistently fitted with three symmetric doublets. With annealing the areal fractions of two of the doublets increased to 44% and 48 %, respectively, while that of the third doublet decreased to be replaced by a single line component with isomer shift δ = 0.0 mm/s. Comparison of the observed isomer shifts with recent in-beam Mossbauer measurements and theoretical calculations allow us to attribute the singlet to intersti…