Structural and electrochemical investigation on re-cast Nafion membranes for polymer electrolyte fuel cells (PEFCs) application

Abstract Starting from a 5 wt% ion power Nafion® solution and dissolving the dry residue in a suitable solvent (10 wt% solution in dimethylacetammide), re-cast Nafion films were developed for polymer electrolyte fuel cells (PEFCs) application. The used Doctor-Blade casting technique allowed to prepare scaled-up membranes comparable to the commercial Nafion ones with good mechanical resistance, thickness homogeneity and an excellent reproducibility. The differences between the re-cast membrane nanostructure and that of the commercial Nafion were investigated by synchrotron small-angle X-ray scattering. The obtained re-cast membrane shows at ambient conditions a semi-crystalline structure wit…

Functionalised Hybrid Poly(ether ether ketone): a Hydrogen Storage Material

Progress in polymeric material for hydrogen storage application in middle conditions

Hydrogen sorption using a manganese oxide anchored to PEEK (Poly(ether-ether-keton)) matrix was studied. The functionalization process and the obtained results on hydrogen storage capability of the synthesized polymer are reported. The functionalised polymer was characterised by Scanning Electron Microscopy, Transmission Electron Microscopy, X-ray diffraction and Volumetric Hydrogen sorption measurements. Different synthesis conditions in terms of precursor concentration and reaction time were used and the direct correlation between manganese oxide percentage and hydrogen storage capability was confirmed. In this way different powders were synthesised. It is assumed that the sample with 78 …