Andris Cimmers
The Suitability of Chemically and Thermally Activated Quaternary Clays of Latvia as Raw Material for Geopolymer Binders
It is now accepted that new binders are needed to replace Portland cement (PC) for enhanced environmental and durability performance. The urge to reduce emissions of carbon and the fact that PC structures having built a few decades ago are already facing disintegration problems points out the handicaps of PC binders. Research works carried out in developing of alkali-activated binders show that this new type of binder could have a huge potential to become as alternative building material. Latvian Quaternary clays were studied from the point of view of the national economy, analysing the physical properties and chemical composition of those sediments in connection with the possibilities of …
Suitability of Illite Based Clays of Latvia for Chemical and Thermal Activation
Materials has been synthesized in the temperature range from 600-800 0C from illite based clays of Latvia under activation of KOH and NaOH solutions (4-6 M). Compressive strength and apparent porosity were measured. The effect of the concentration of KOH and NaOH solutions on the material mechanical properties was investigated by means of infrared spectroscopy (IR). Compressive strength data of the materials showed that via such activation building materials with good quality can be obtained.
Mechanical properties of materials obtained via alkaline activation of illite-based clays of Latvia
Materials has been synthesized in the temperature range from 60-100 °C from two illite based clays of Latvia under activation of KOH and NaOH solutions (4-6 M). Compressive strength and apparent porosity were measured. The effect of concentration of KOH and NaOH solutions on the material mechanical properties was investigated by means of infrared spectroscopy (IR). Compressive strength data of the materials showed that via such activation could obtain building materials with good quality.