Ilmari Hiidenheimo
Amorphous and crystalline polyetheretherketone: Mechanical properties and tissue reactions during a 3-year follow-up.
The study was aimed to test the mechanical strength, structural stability, and tissue reactions of optically amorphous and crystalline polyetheretherketone (PEEK) plates during a 3-year follow-up in vivo and in vitro. The injection-moulded PEEK plates were implanted to the dorsal subcutis of 12 sheep, which were sacrificed at 6-156 weeks. Thereafter, the plates were subjected to tensile tests, and levels of crystallinity were assessed by differential scanning calorimetry (DSC). Histological evaluation was carried out using the paraffin technique. In vitro properties were examined with the tensile test and DSC at 0-156 weeks. Tissue reactions were mild and fairly similar for the amorphous an…
In vivo and in vitro degradation of a novel bioactive guided tissue regeneration membrane
The aim of this study was to assess degradation of a novel bioactive guided tissue regeneration (GTR) membrane and to quantify the concurrent tissue responses. Pieces of membrane composed of poly-l-lactide, poly-d,l-lactide, trimethylenecarbonate and polyglycolide were dipped into an N-methyl-2-pyrroline (NMP) solution and implanted in the mandibles of 10 sheep. The animals were sacrificed at 6-104 weeks. Parallel in vitro degradation was analysed by measuring the inherent viscosity, water absorption and remaining mass. One of the 2 in vitro sets of membranes was prehandled with NMP. At 6-26 weeks in vivo, the gradually more degraded implants were surrounded by a fibrous network. At 52 and …