Luminescence of dense, octahedral structured crystalline silicon dioxide (stishovite)

Abstract It is obtained that, as grown, non-irradiated stishovite single crystals possess a luminescence center. Three excimer pulsed lasers (KrF, 248 nm; ArF, 193 nm; F 2 , 157 nm) were used for photoluminescence (PL) excitation. Two PL bands were observed. One, in UV range with the maximum at 4.7±0.1 eV with FWHM equal to 0.95±0.1 eV, mainly is seen under ArF laser. Another, in blue range with the maximum at 3±0.2 eV with FWHM equal to 0.8±0.2 eV, is seen under all three lasers. The UV band main fast component of decay is with time constant τ =1.2±0.1 ns for the range of temperatures 16–150 K. The blue band decay possesses fast and slow components. The fast component of the blue band deca…