Strain-induced improvement of retention loss in PbZr0.2Ti0.8O3 films

The retention behavior of nanoscale domains in PbZr0.2Ti0.8O3 thin films is investigated by in-situ controlling the epitaxial strain arising from a piezoelectric substrate. The retention behavior in our sample shows strong polarity-dependence: Upward-poled domains exhibit excellent stability, whereas downward-poled domains reveal a stretched exponential decay. Reversible release of in-plane compressive strain strongly reduced the retention loss, reflected in an enhancement of the relaxation time by up to one order of magnitude. We tentatively attribute the observed behavior to a strain dependence of the built-in field at the interface to the La0.7Sr0.3MnO3 bottom electrode, with a possible …