Molybdenum oxide nitrides of the Mo_{2}(O,N,\square)_{5}$ type : on the way to Mo_{2}O_{5}$
Abstract: Blue-colored molybdenum oxide nitrides of the Mo-2(O,N,square)(5) type were synthesized by direct nitridation of commercially available molybdenum trioxide with a mixture of gaseous ammonia and oxygen. Chemical composition, crystal structure, and stability of the obtained and hitherto unknown compounds are studied extensively. The average oxidation state of +5 for molybdenum is proven by Mo K near-edge X-ray absorption spectroscopy; the magnetic behavior is in agreement with compounds exhibiting (MoO6)-O-v units. The new materials are stable up to similar to 773 K in an inert gas atmosphere. At higher temperatures, decomposition is observed. X-ray and neutron powder diffraction, e…
Crystal chemical characterization of mullite-type aluminum borate compounds
Abstract Al-rich aluminum borates were prepared by different synthesis routes using various Al/B ratios, characterized by diffraction methods, spectroscopy and prompt gamma activation analysis. The 11B NMR data show a small amount of BO4 species in all samples. The chemical analysis indicates a trend in the Al/B ratio instead of a fixed composition. Both methods indicate a solid solution Al5−xB1+xO9 where Al is substituted by B in the range of 1–3%. The structure of B-rich Al4B2O9 (C2/m, a=1488 pm, b=553 pm, c=1502 pm, s=90.6°), was re-investigated by electron diffraction methods, showing that structural details vary within a crystallite. In most of the domains the atoms are orderly distrib…
Two stage magnetic ordering and spin idle behavior of the coordination polymer Co3(OH)2(C4O4)2·3H2O determined using neutron diffraction.
We report the magnetic structure of two of the magnetically ordered phases of Co(3)(OH)(2)(C(4)O(4))(2)·3H(2)O, a coordination polymer that consists of a triangular framework decorated with anisotropic Co(II) ions. The combination of neutron diffraction experiments and magnetic susceptibility data allows us to identify one phase as displaying spin idle behavior, where only a fraction of the moments order at intermediate temperatures, while at the lowest temperatures the system orders fully. This novel magnetic behavior is discussed within the framework of a simple Hamiltonian and representational analysis and rationalizes this multiphase behavior by considering the combination of frustratio…