Effect of antisite defects on the magnetic properties of ZnFe2 O4

2013

Magnetic zinc ferrite (ZnFe2O4) nanopowders were synthesized using the sol–gel autocombustion method. X-ray diffraction (XRD) and scanning electron microscopy (SEM) measurements demonstrated that thermal decomposition of the 1-mm-thick xerogel layers in air formed monophasic spinel ferrite nanopowders with a particle size less than 30 nm. X-ray photoelectron spectroscopy (XPS) showed that the obtained reaction product contained antisite defects, with zinc ions occurring at the octahedral sites of the spinel structure. The concentration of antisite defects or inversion degree decreased when the relatively low annealing temperature was increased from 150 to 500 °C. Overall, the obtained ZnFe2…