FATIGUE LIFE ANALYSIS OF RAIL-WELDS USING LINEAR ELASTIC FRACTURE MECHANICS

The initiation and growth of fatigue cracking is mainly due to high stress concentration, heterogeneity and poor quality of weld. The detection and rectification of such weld defects are major concerns of rail network managers to reduce potential risk of rail breaks and derailments. To estimate the fatigue life of welded joints and to analyze the progress of fatigue cracks, a fracture mechanics-based analysis and fatigue models were developed using Finite Element Analysis. The initial flaw is obtained from a sample weld using ultrasonic flaw detecting machine test. Linear Elastic Fracture Mechanics (LEFM) approach based on the Paris law was applied to determine critical crack size and the n…