Evaluation of microhardness, sorption, solubility, and color stability of bulk fill resins : a comparative study
2020
Background Due to the increasing popularity of bulk fill resins, there is a concern that their components can be leached; this is because these are inserted in a single 4-5 mm increment. This in vitro study evaluated the microhardness, sorption, solubility, and color stability of three restorative bulk fill resins, namely: Filtek Bulk Fill (FBF), Tetric N-Ceram Bulk Fill (TNC), and Opus Bulk Fill (OBF). Material and Methods Cylindrical samples were fabricated to be 15 mm in diameter and 1 mm thick (n = 10). For the microhardness test, three random indentations were formulated on the samples using a micro-durometer with a load of 300 gf for 15 s. Sorption and solubility were then evaluated (…
Influence of different thermopolymerization methods on composite resin microhardness
2020
Background Additional heat polymerization in composite resins allows greater effectiveness of microhardness, flexural strength, fracture toughness, wear resistance, and increased color stability. Material and Methods 150 composite resin specimens were made using a 4 mm diameter and 2 mm thick bipartite steel matrix. Five resins composed of different compositions were tested (Brilliant Everglow/Coltene, Filtek One BulkFill/3M, Filtek P60/3M, Filtek Z350XT/3M, Filtek Z250XT/3M), and for each of them three types of polymerization were tested: light curing only (n=50); photopolymerization + autoclave thermopolymerization (n=50) and photopolymerization + microwave thermopolymerization (n=50). …