Catalytic performance of CoAlZn and NiAlZn mixed oxides in hydrogen production by bio-ethanol partial oxidation

CoAlZn and NiAlZn mixed oxides were prepared by sol-gel method and tested in partial oxidation of bio-ethanol (POE). At lower temperatures, CoAlZn showed higher ethanol conversion and higher selectivity to H2 and CO than NiAlZn. At higher temperatures, ethanol conversion on both catalysts reached 100%, while selectivity (S) to H2 and CO became higher on NiAlZn. At 750 C, NiAlZn showed S(H2) of 95%, S(CO) of 90%, while for CoAlZn these values were 90% and 83% respectively. Both catalysts were resistant to coking, but the amount of carbon deposits was still lower on NiAlZn. During 50 h on-stream, ethanol conversion and selectivity to H2 and CO on NiAlZn remained unchanged demonstrating stable…