Photoluminescence excitation spectroscopy in boron nitride nanotubes compared to microcrystalline h‐BN and c‐BN
Photoluminescence spectra and photoluminescence excitation spectra have been measured on samples of hexagonal boron nitride microcrystalline powder, cubic boron nitride single crystal, and boron nitride nanotubes (mixture of single-walled and multi-walled with some h-BN precursor). The reason for studying these 3 samples in a comparative fashion is that nanotube BN, while based on a rolled hexagonal-BN (sp2-bonded) sheet, is expected to take on more sp3 bond-character reminiscent of cubic-BN as the curvature becomes tighter. With some simplicity of statement, this study was planned to view spectroscopy of nanotube BN with respect to its two limiting cases of bond character, all measured in …
Exciton luminescence of boron nitride nanotubes and nano-arches
We report photoluminescence (PL) and PL-excitation spectroscopy of BN nanotubes (nt-BN) mixed with some residual hexagonal crystalline (h-BN) starting material, and of pure h-BN microcrystalline powder. The nanotube phase exhibits a broad-band PL near 380 nm, in agreement with a published report of cathodoluminescence from a sample comprising >90% nanotubes. This emission is almost 3 eV lower in energy than unrelaxed exciton states found in recent all-electron theories of nt-BN and h-BN and about 1.4 eV lower than the lowest (perturbed dark?) exciton seen in absorption of nt-BN. This may suggest that excitons in nt-BN vibrationally relax to self-trapped states before emitting, a path found …