Structural and hydrogenation study on the ball milled TiH2–Mg–Ni

2015

International audience; With the aim of further understanding for TieNieMg alloys and their hydrogenation behavior, powders of TiH2, Mg and Ni with the molar ratio of 3:1:2 have been mechanically milled for 10 h, 20 h, 30 h, 40 h according to the stoichiometry (TiH2)1.5Mg0.5Ni. Microstructures of the milled sample were analyzed and their hydrogenation properties as negative electrodes for Ni-MH batteries were studied. Phase change with milling time revealed the fast formation of the Ti-Mg-H FCC phase. The alloying priority among Ti, Mg and Ni was demonstrated by comparing phase compositions in different milling time. Hydrogen capacities evaluated by both solidegas reaction and electrochemic…