Atomic layer deposition of AlN from AlCl3 using NH3 and Ar/NH3 plasma
The atomic layer deposition (ALD) of AlN from AlCl3 was investigated using a thermal process with NH3 and a plasma-enhanced (PE)ALD process with Ar/NH3 plasma. The growth was limited in the thermal process by the low reactivity of NH3, and impractically long pulses were required to reach saturation. Despite the plasma activation, the growth per cycle in the PEALD process was lower than that in the thermal process (0.4 Å vs 0.7 Å). However, the plasma process resulted in a lower concentration of impurities in the films compared to the thermal process. Both the thermal and plasma processes yielded crystalline films; however, the degree of crystallinity was higher in the plasma process. The fi…
Tribological properties of thin films made by atomic layer deposition sliding against silicon
Interfacial phenomena, such as adhesion, friction, and wear, can dominate the performance and reliability of microelectromechanical (MEMS) devices. Here, thin films made by atomic layer deposition (ALD) were tested for their tribological properties. Tribological tests were carried out with silicon counterpart sliding against ALD thin films in order to simulate the contacts occurring in the MEMS devices. The counterpart was sliding in a linear reciprocating motion against the ALD films with the total sliding distances of 5 and 20 m. Al2O3 and TiO2 coatings with different deposition temperatures were investigated in addition to Al2O3-TiO2-nanolaminate, TiN, NbN, TiAlCN, a-C:H [diamondlike car…
Atomic layer deposition of AlN from AlCl3 using NH3 and Ar/NH3 plasma
The atomic layer deposition (ALD) of AlN from AlCl3 was investigated using a thermal process with NH3 and a plasma-enhanced (PE)ALD process with Ar/NH3 plasma. The growth was limited in the thermal process by the low reactivity of NH3, and impractically long pulses were required to reach saturation. Despite the plasma activation, the growth per cycle in the PEALD process was lower than that in the thermal process (0.4A ° vs 0.7A ° ). However, the plasma process resulted in a lower concentration of impurities in the films compared to the thermal process. Both the thermal and plasma processes yielded crystalline films; however, the degree of crystallinity was higher in the plasma process. The…