Synthesis of Eu2+ and Dy3+ Doped Strontium Aluminates and their Properties
2017
Financial support to this project was provided by National Research Programme (IMIS2).
Synthesis of Eu<sup>2+</sup> and Dy<sup>3+</sup> Doped Strontium Aluminates and their Properties
2016
Strontium aluminate phosphors were synthesized by the solution combustion method using citric acid, urea or glycine as reducing agent and europium and dysprosium as dopants. The content of both dopants was in the range of 1 – 2 mol%. Dependence of phase composition, crystallite size and specific surface area on calcinations temperature, used reducing agents and dopants were determined. Luminescent properties of the calcinated at 1300 °C powders contained SrAl2O4 (90 %) and Sr4Al24O25 (10%) phases with crystallite size of 80 nm were determined.
Flekainīda bāzes polimorfo formu un hidrāta iegūšana un stabilitāte
2011
Flekainīda bāze ir farmaceitiski aktīvās vielas flekainīda acetāta izejviela. Pētīts flekainīda bāzes polimorfisms, hidrāta veidošanās un vielas stabilitāte dažādās temperatūrās un mitrumos, aprēķināti flekainīda bāzes formas Ib kristāliskā režģa parametri un noteikta struktūra pēc pulvera rentgendifraktometrijas datiem.
Ar Eu2+ un Dy3+ dopētu stroncija aluminātu nanodaļiņu sintēzes metožu izstrāde un to īpašības
2015
Maģistra darbā aprakstītas dažādas stroncija aluminātu sintēzes metodes un stroncija aluminātu fāzes. Veikta stroncija aluminātu sintēze ar šķīduma–degšanas metodi, par degšanas aģentiem izmantojot organiskas vielas un par dopantiem – dažādas koncentrācijas eiropiju un disproziju. Sintezēto vielu kvalitatīvā analīze veikta ar pulvera rentgendifraktometriju, noteikta īpatnējā virsma un mētīta fotoluminiscence.