X-RAY PHOTOEMISSION ELECTRON MICROSCOPE DETERMINATION OF ORIGINS OF ROOM TEMPERATURE FERROMAGNETISM AND PHOTOLUMINESCENCE IN HIGHCo-CONTENTCoxZn1-xOFILMS

In this paper, we reported on the X-ray photoemission electron microscope (XPEEM) determination of magnetic and luminescence origins for two CoxZn1-xO films. The cobalt fraction x of radio frequency co-sputtered samples were 0.86(2) and 0.92(2), respectively. Films were ferromagnetic and semiconductive. Unique narrow green color lines beside the ZnO intrinsic emissions were found with a decay time in microsecond range at room temperature. Origins of magnetic and luminescence properties were determined with XPEEM. The X-ray absorption near edge structure at the Co  L3-edge denoted that Co was partially oxidized, and phase-contrast images together with chemical composition identification furt…