0000000000901757
AUTHOR
G. Vitins
Synthesis and structural and ionic conductivity studies of Na2ZrSi4O11
The compound Na 2 ZrSi 4 O 1 1 has been prepared both by solid state synthesis and by the sol-gel technique via alkoxides. The structure of Na 2 ZrSi 4 O 11 was investigated by the Rietveld method using X-ray diffractometer data. The powder diffraction data show evidence for a triclinic distortion of the basic monoclinic structure. The ionic conductivity has been determined in the temperature interval 130-560°C using a.c. impedance measurements. The Na + ion mobility is limited, with E a =1.04 eV and σ(300°C)= 2-9 10 7 S/cm. Samples with Ta partially substituted for Zr, according to the formula Na 2-x (Zr 1-x Ta x )Si 4 O 11 with x ≤0.2, showed the same evidence for a triclinic distortion. …
Application of sol-gel and laser evaporation methods to obtain thin gas sensitive films
New type resistive/capacitative gas sensitive structures were obtained by using a specially prepared substrate- glass, covered by thin conducting In/sub 2/O/sub 3/ layer, cutted into a comb teeth-type electrodes by help of laser beam. Such laser processed gap in the layer of conducting material was a prototype of excellent humidity sensor, especially at high values of relative humidity (RH). Different additional coatings onto a laser processed gap were examined for humidity sensing. Sol-gel, vacuum thermal evaporation and laser evaporation methods were used to obtain a thin layers of different materials.