Flux-flow instability and its anisotropy inBi2Sr2CaCu2O8+δsuperconducting films
We report measurements on voltage instability at high flux-flow velocities in ${\mathrm{Bi}}_{2}{\mathrm{Sr}}_{2}{\mathrm{CaCu}}_{2}{\mathrm{O}}_{8+\mathrm{\ensuremath{\delta}}}$ superconducting films. Current-voltage $(I\ensuremath{-}V)$ characteristics have been measured as a function of temperature, magnetic field, and angle between the field and the c axis of the sample. Voltage jumps were observed in $I\ensuremath{-}V$ characteristics taken in all magnetic-field directions and in extended temperature and field ranges. An analysis of the experimental data, based on a theory for viscous flux-flow instability with a finite heat-removal rate from the sample, yielded the inelastic scatterin…
Preparation and characterization of (Hg0.7Mo0.3)Sr2(Ca0.7Y0.3)Cu2Ox and (Hg0.9Re0.1)Ba2CaCu2Oy superconducting films by laser ablation
Abstract Oriented (Hg 0.7 Mo 0.3 )Sr 2 (Ca 0.7 Y 0.3 )Cu 2 O x and (Hg 0.9 Re 0.1 )Ba 2 CaCu 2 O y superconducting films were prepared on SrTiO 3 substrates using laser ablation and post-Hg-vapor annealing. Due to the stability of Mo 0.3 Sr 2 (Ca 0.7 Y 0.3 )Cu 2 O x and Re 0.1 Ba 2 CaCu 2 O y in air, no special handling was needed during the grinding, mixing and pressing of the precursor targets. The superconductivity of the films was characterized with the temperature dependence of the ac susceptibility ( χ - T ) and the resistance ( R - T ) while the crystallography was probed with x-ray diffraction (XRD) and scanning electron microscopy (SEM).