Mechanical properties and corrosion behaviour after scratch and tribological tests of electrodeposited Co-Mo/TiO2 nano-composite coatings

2019

International audience; The micro-mechanical (Young’s modulus and hardness) and tribological properties, as well as the scratch resistance of Co-Mo/TiO2 nano-composite coatings were investigated. The coating was found to be harder and stiffer than the substrate (pure cobalt). Low residual stresses were also derived from Stoney’s equation (type I stress). The corrosion behaviour after tribological and scratch tests was studied in Ringer’s solution. Dry sliding of the coating against an alumina ball at the load of 1 N or 2 N over the same distance had nearly no influence onthe anodic branch of the polarisation curves. By contrast, the current density in the cathodic branch (oxygen reduction r…