Passive and transpassive behaviour of Alloy 31 in a heavy brine LiBr solution
The passive and transpassive behaviour of Alloy 31, a highly alloyed austenitic stainless steel (UNS N08031), has been investigated in a LiBr heavy brine solution (400 g/l) at 25 °C using potentiostatic polarisation combined with electrochemical impedance spectroscopy and Mott–Schottky analysis. The passive film formed on Alloy 31 has been found to be p-type and/or n-type in electronic character, depending on the film formation potential. The thickness of the film formed at potentials within the passive region increases linearly with applied potential. The film formed at transpassive potentials is thinner and more conductive than the film formed within the passive region. These observations…
Thermogalvanic effects on the corrosion of copper in heavy brine LiBr solutions
Thermogalvanic corrosion of copper in heavy brine LiBr solutions has been investigated using a zero-resistance ammeter (ZRA). The temperature gradients between copper electrodes immersed in the same LiBr solution result in the formation of thermogalvanic cells with hot anodes, leading to high and sustained thermogalvanic currents. Copper loss rates, calculated using Faraday's law, substantially exceed 0.025mmyear -1, a value regarded as the threshold of low corrosion rates. The effects of thermogalvanic coupling on the surface properties of the anode and the cathode have been analysed by means of electrochemical impedance spectroscopy (EIS). The results obtained in this analysis have been r…