Weak itinerant ferromagnetism and electronic and crystal structures of alkali-metal iron antimonides: NaFe4Sb12andKFe4Sb12
2004
The synthesis, chemical, structural, and magnetic properties of alkali-metal compounds with filled-skutterudite structure, $\mathrm{Na}{\mathrm{Fe}}_{4}{\mathrm{Sb}}_{12}$ and $\mathrm{K}{\mathrm{Fe}}_{4}{\mathrm{Sb}}_{12}$, are described. X-ray and neutron diffraction and elemental analysis established the crystal structure without defects and disorder on the cation site. The temperature and pressure dependence of the cubic unit cell of $\mathrm{Na}{\mathrm{Fe}}_{4}{\mathrm{Sb}}_{12}$ and the displacement parameter of Na are investigated. The electronic structure is calculated by density functional methods (LMTO, FPLO). Quantum chemical calculations (electron localization function) reveal …
Spark Plasma Sintering à partir de poudres mécaniquement activées : compréhension des transitions de phase au cours d'un frittage réactif
2007
International audience; À " basse température " (entre 400 et 600 ◦C), l'oxydation de MoSi2 entraîne sa désintégration en poudre (phénomène de " peste "). De récents travaux ont montré que l'utilisation de MoSi2 dense et nano-organisé permettrait de ralentir ce phénomène de " peste ". Le défi de produire des matériaux denses et nano-organisés peut être relevé par le frittage " flash " réactif sous champ électrique à partir des poudres mécaniquement activées (Mechanically-Activated Spark Plasma Sintering, MASPS). Le contrôle de la composition et de la microstructure du composé intermétallique MoSi2 nécessite de déterminer les paramètres du frittage SPS (température, rampe de montée en tempér…