Correlation between polymer architecture, mesoscale structure and photovoltaic performance in side-chain-modified poly(p-arylene-ethynylene)-alt-poly(p-arylene-vinylene): PCBM bulk-heterojunction solar cells
Abstract Recent investigations have shown that an anthracene containing poly( p -arylene-ethynylene)-alt-poly( p -arylene-vinylene) statistical copolymer consisting of a well defined conjugated backbone, along which linear and branched alkoxy side chains are attached in a random manner, yields, compared to its counterparts with regular side chain substitution, an improved performance in polymer [6,6]:-phenyl-C 61 -butyric acid methyl ester (PCBM) bulk-heterojunction solar cells. The microscopic origin for the improved power conversion efficiency ( η ≈ 3.8%) of the statistical copolymer – which is the best in its material class – has not been resolved. We conducted grazing incidence wide-an…
Nucleation and crystal growth in a suspension of charged colloidal silica spheres with bi-modal size distribution studied by time-resolved ultra-small-angle X-ray scattering
A suspension of charged colloidal silica spheres exhibiting a bi-modal size distribution of particles, thereby mimicking a binary mixture, was studied using time-resolved ultra-small-angle synchrotron X-ray scattering (USAXS). The sample, consisting of particles of diameters d(A) = (104.7 ± 9.0) nm and d(B) = (88.1 ± 7.8) nm (d(A)/d(B) ≈ 1.2), and with an estimated composition A(0.6(1))B(0.4(1)), was studied with respect to its phase behaviour in dependance of particle number density and interaction, of which the latter was modulated by varying amounts of added base (NaOH). Moreover, its short-range order in the fluid state and its eventual solidification into a long-range ordered colloidal…