Peculiarities of luminescent properties of cerium doped YAG transparent nanoceramics
2010
Abstract Optical and luminescence properties of transparent nanosized cerium doped Y 3 Al 5 O 12 (YAG:Ce) ceramics have been studied. YAG:Ce nanoceramics were obtained by means of low temperature and high pressure (LTHP) sintering method. Nanoceramic samples were sintered in the 2–8 GPa pressure range, whereas Ce 3+ concentration was varied in the 0.5–5 at. % range. It is shown that, in contrast to the single crystal, a strong rise of absorption coefficient was detected already at wavelength shorter than 400 nm in all nanoceramic samples studied. Furthermore, in nanoceramic samples unusual UV emission band near 3.1 eV was observed, which is not observed in the YAG:Ce single crystal. High pr…
Ce:Y3Al5O12−Poly(methyl methacrylate) Composite for White-Light-Emitting Diodes
2014
A Ce:YAG-poly(methyl methacrylate) (PMMA) composite was prepared by using the melt compounding method. The structure and morphology were investigated by X-ray diffractometry, transmission electron microscopy, and small-angle X-ray scattering. The optical properties (emission, excitation, and fluorescence decay rate) of the composite were studied by using photoluminescence spectroscopy. The polymer–filler interactions were studied using 13C cross-polarization magic-angle spinning NMR spectroscopy (13C{1H} CP-MAS NMR). The results indicated that Ce:YAG particles are well-dispersed in the PMMA matrix without loss of their luminescence properties or significant spectral shift, thus suggesting t…