Investigation of La2O3 and/or (Co,Mn)3O4 deposits on Crofer22APU for the SOFC interconnect application

International audience; Chromia forming alloys (stainless steels) are among the best candidates for SOFC interconnects. However, problems of decreasing electronic conductivity during high temperature service and volatility of chromium oxide scales need to be solved. Electronically conductive surface coatings, which also reduce oxide scale growth and chromium volatility, are needed to improve stainless steel interconnects. The goal of this study is to investigate combinations of lanthanum oxide (La2O3) and cobalt manganese oxide ((Co,Mn)3O4) coatings on Crofer22APU stainless steel. Thin film coatings of La2O3 (~200 nm) and Co,Mn (1:1) (~2 mm) were deposited via metal organic chemical vapor d…